High Impact Polystyrene/Virgin& Recycled HIPS
Specification:
Property
Unit
Test Method
Test Condition
HIPS
Tensile Strength
kg/cm2
(Â MPa)ASTMÂ D-638
( ISO527)23°C
220
(22)
Tensile Elongation
%
ASTMÂ D-638
( ISO527)23°C
40
Flexural Strength
kg/cm2
(Â MPa)ASTMÂ D-790
( ISO178)23°C
440
(43)
Flexural Modulus
kg/cm2*104
(Â MPa)ASTMÂ D-790
( ISO178)23°C
2.3
(2260)
Izod
Impact Strengthkg-cm/cm
( J/m )ASTM D-256
( ISO R180 )23°C
1/4''Â bar11.0
(108)
Vicat Softening
Temperature°C
ASTMÂ D-1525
(ISO306B)Annealed
80°C×2Hr
1/8''Â bar95
Heat Deflection
Temperature°C
ASTMÂ D-648
(Â 75/A)Annealed
80°C×2Hr
1/8''Â bar88
Melt
Flow Indexg/10 min
ASTMÂ D-1238
( ISO1133 )200°C×5Kg
(Â 49NÂ )5.5
Residual Monomer
ppm max.
-Â
-Â
700
MoldingÂ
Shrinkage%
FCFC
Method23°C
0.4~0.6
Specific Gravity
-
ASTMÂ D-792
( ISO1183 )23°C/23°C
1.04
Flammability
-
UL-94
FILEÂ NO.
E1628231/16"Â HB
NC
HIPS-688
Raw materials description
Standard
Injection molding grade
Colour
White
Application
High impact, high heat-resisting, low temperature resistance,good regidity,according with food hygienic standard, be widely used in toy and home appliances manufacture.
Remark
High impact, high heat-resisting, extrusion molding.
Raw materials technique data
Property items
Test condition
Method
Test result
Units
Basic performance
Melt flow rate
200°C/5kg
ISO 1133
4.6
g/10min
Density
 ISO 1183
1.04
g/cm3
Water absorption
 ISO 62
<0.1
%
Physical property
Process contractibility rate
 ISO 294
0.4-0.7
%
Mechanical behavior
Stretch yield stress
23°C
ISO 527
23
Mpa
Percentage elongation
23°C
ISO 527
45
%
flexural strengh
23°C
ISO 178
46
Mpa
Flexural modulus
23°C
ISO 178
2260
Mpa
Izod impact
23°C
ISO 180
115
j/m
Rockwell hardness
23°C
ASTMD-785
65
L
Thermal propertyVicat softening point
B10/oil
ISO 306
95
°C
distortion temperature(non-anneal)
1.82Mpa
ISO 75-2
79
°C
Other propery
Fire resistance
 UL 94
HB
Â
residual monomer
Â
 <400
ppm max
Â
Â
Â
Â
Â
Â
Â
Â
Hot Sale Virgin&Recycled Manufacturer HIPS