Call Us Anytime With Questions About Your Application. More information , pls feel free to contact Ms Lydia: Mobile :86-18988789546 Call Us Anytime With Questions About Your Application. More information , pls feel free to contact Ms Lydia: Mobile :86-18988789546 Baoji zhipu non-ferrous metal processing co., LTD. Main processing single crystal furnace, vacuum furnace, furnace, such as sapphire molybdenum, tungsten, tantalum, niobium tungsten bars, tungsten bars, tungsten thermal field pipe fittings such as deep processing, domestic use of the best quality raw materials, equipped with advanced equipment and professional production team, welcome to inquire, looking forward to your cooperation! Tantalum Bar,Good Stability Tantalum Bar,High Purity Tantalum Bar,Polished Tantalum Bar Baoji Zhipu Non-Ferrous Metals Processing Co., Ltd. , http://www.czpmow.com
1. Applications for Tin cured silicone rubber for artificial stone casting:
Production mold casting wax, gypsum, concrete or resins (urethane, polyester, etc. ). Applications include reproducing sculpture, architectural restoration, making candle molds, casting pewter, place couldnt pour rubber over the above etc. For make a mold by brushing (or spraying) rubber onto the model. Rubber will hold a vertical surface and will reproduce the finest detail brushed onto the model in layers until a suitable thickness is built up. The rubber is allowed to cure and a support shell is applied prior to demold. The advantage of making a mold by brushing rubber onto the model is that it minimizes the amount of rubber used, saving material costs.
2. Properties for Tin cured silicone rubber for artificial stone casting:
Brushable Silicone Rubber for Plaster Casting Cornice/Domes Mold that have the best release properties for production casting of resins, plaster, etc. It is a tin silicone rubber that self-thickens for making concrete Spray able -on molds. Properly applied, Mixed 100A: 5B by weight, rubber quickly develops thixotropy when mixed in air. Cured with negligible shrinkage to a durable mold rubber good for production casting resins, foams, concrete, plaster and other materials. Application of a support shell is achieved by spraying over the rubber mold after it has fully cured.
3. Datasheet for Tin cured silicone rubber for artificial stone casting:
Model: HY-630
Appearance: White
Mixing proportion of curing agent (%): 5%
Operating time (mins 25 0C ): 60-90
Curing time(hours 25 0C): 5-7
Hardness (A° ): 30± 2
Viscosity (Mpas -25 0C): 27000~32000
Tensile-strength(Mpa): >4.2
Tear-strength (KN/m): >30
Elongation-break(%): > 440
Linear Shrinkage (%): <0.3
4. Using instruction for Tin cured silicone rubber for artificial stone casting:
Component A is white flowing liquid and component B is the curing agent. For example, take silicone rubber of 100g and add 2g curing agent for mixing evenly (silicone rubber and curing agent must be measured accurately). After the silicone rubber and the curing agent are completely mixed, put the silicon into a vacuum machine for deairing to remove the bubbles. After deaired, pouring the liquid silicone rubber into the product to be duplicated or into the mold frame. If you don't have vacuum machine, please add 1.2% or 1.5% curing agent so that the bubbles can bubble itself. Since the less curing agent you add, the slower the mould will curdle, the bubbles will bubble out itself.
5. Package for Tin cured silicone rubber for artificial stone casting:
25kg/drum or 200kg/drum
Item
Mixing Ration
Color
Viscosity (cps)
Hardness
Operating Time (25°)
Curing Time (25°)
Tear-strength(kN/m)
Tensile-strength(Mpa)
610
100:4
White
11000±3000
10±3
30-50 mins
3-4h
16±2
≥2.8
615
100:4
White
12000±3000
15±3
30-50 mins
3-4h
19±2
≥2.8
620
100:4
White
15000±3000
20±3
30-50 mins
3-4h
24±2
≥2.8
625
100:4
White
25000±3000
25±3
30-50 mins
3-4h
26±2
≥3.4
630
100:4
White
27000±3000
30±3
30-50 mins
3-4h
26±2
≥4.2
635
100:4
White
30000±3000
35±3
30-50 mins
3-4h
25±2
≥4.5
640
100:4
White
15000±3000
40±3
30-50 mins
3-4h
21±2
≥3.5
Tel:Â Â (00)Â 86-755-89948019
1. Applications for Tin cured silicone rubber for artificial stone casting:
Production mold casting wax, gypsum, concrete or resins (urethane, polyester, etc. ). Applications include reproducing sculpture, architectural restoration, making candle molds, casting pewter, place couldnt pour rubber over the above etc. For make a mold by brushing (or spraying) rubber onto the model. Rubber will hold a vertical surface and will reproduce the finest detail brushed onto the model in layers until a suitable thickness is built up. The rubber is allowed to cure and a support shell is applied prior to demold. The advantage of making a mold by brushing rubber onto the model is that it minimizes the amount of rubber used, saving material costs.
2. Properties for Tin cured silicone rubber for artificial stone casting:
Brushable Silicone Rubber for Plaster Casting Cornice/Domes Mold that have the best release properties for production casting of resins, plaster, etc. It is a tin silicone rubber that self-thickens for making concrete Spray able -on molds. Properly applied, Mixed 100A: 5B by weight, rubber quickly develops thixotropy when mixed in air. Cured with negligible shrinkage to a durable mold rubber good for production casting resins, foams, concrete, plaster and other materials. Application of a support shell is achieved by spraying over the rubber mold after it has fully cured.
3. Datasheet for Tin cured silicone rubber for artificial stone casting:
Model: HY-630
Appearance: White
Mixing proportion of curing agent (%): 5%
Operating time (mins 25 0C ): 60-90
Curing time(hours 25 0C): 5-7
Hardness (A° ): 30± 2
Viscosity (Mpas -25 0C): 27000~32000
Tensile-strength(Mpa): >4.2
Tear-strength (KN/m): >30
Elongation-break(%): > 440
Linear Shrinkage (%): <0.3
4. Using instruction for Tin cured silicone rubber for artificial stone casting:
Component A is white flowing liquid and component B is the curing agent. For example, take silicone rubber of 100g and add 2g curing agent for mixing evenly (silicone rubber and curing agent must be measured accurately). After the silicone rubber and the curing agent are completely mixed, put the silicon into a vacuum machine for deairing to remove the bubbles. After deaired, pouring the liquid silicone rubber into the product to be duplicated or into the mold frame. If you don't have vacuum machine, please add 1.2% or 1.5% curing agent so that the bubbles can bubble itself. Since the less curing agent you add, the slower the mould will curdle, the bubbles will bubble out itself.
5. Package for Tin cured silicone rubber for artificial stone casting:
25kg/drum or 200kg/drum
Item
Mixing Ration
Color
Viscosity (cps)
Hardness
Operating Time (25°)
Curing Time (25°)
Tear-strength(kN/m)
Tensile-strength(Mpa)
610
100:4
White
11000±3000
10±3
30-50 mins
3-4h
16±2
≥2.8
615
100:4
White
12000±3000
15±3
30-50 mins
3-4h
19±2
≥2.8
620
100:4
White
15000±3000
20±3
30-50 mins
3-4h
24±2
≥2.8
625
100:4
White
25000±3000
25±3
30-50 mins
3-4h
26±2
≥3.4
630
100:4
White
27000±3000
30±3
30-50 mins
3-4h
26±2
≥4.2
635
100:4
White
30000±3000
35±3
30-50 mins
3-4h
25±2
≥4.5
640
100:4
White
15000±3000
40±3
30-50 mins
3-4h
21±2
≥3.5
Tel:Â Â (00)Â 86-755-89948019
Condensation Molding RTV2 Silicone for Cast Stone Mold
Model NO.: HY-630 silicone for stone
Sticker: Available
Sample: Available
Minimum Order Quantity: 200 Kilogram
Purity: 100%
Certifications: RoHS, MSDS, SGS, ISO9001:2000
Type: Condensation Silicone Rubber
Mixing Ratio: 100:5
Pot Life/Working Life: 30-40 Minutes
Trademark: Hong Ye Silicone Rubber
Specification: SGS. ROHS. MSDS. ISO9001
Origin: China
HS Code: 39100000
Model NO.: HY-630 silicone for stone
Sticker: Available
Sample: Available
Minimum Order Quantity: 200 Kilogram
Purity: 100%
Certifications: RoHS, MSDS, SGS, ISO9001:2000
Type: Condensation Silicone Rubber
Mixing Ratio: 100:5
Pot Life/Working Life: 30-40 Minutes
Trademark: Hong Ye Silicone Rubber
Specification: SGS. ROHS. MSDS. ISO9001
Origin: China
HS Code: 39100000
Tin cured silicone rubber for artificial stone casting
Tin cured silicone rubber for artificial stone casting